CW508L

Dimension

Thickness

Temper

We offer various types of brass sheets to our industrial customers. Sheets are generally available in dimension 1000x2000 mm. We also offer brass plates CW612N stress releived from 15 mm in dimension 1020x3020 mm. The most common alloys are, CW508L, CW503L and CW612N (plates).


  • Dimension: 1000 x 3000 mm
  • Thickness: 0.2
  • Weight: 5,04 kg/stk.
On Request

CW508L

CuZn37 is the major brass alloy for the cold forming process. Even though brasses with lower Zinc content have better cold forming properties, CuZn37 is the most used alloy. Reasons for this are on the one hand economical due to lower price of Zinc compared to Copper, on the other hand the forming properties of this alloy meet the demand of many applications . The alloy type is listed in the USA by EPA to have good antimicrobial properties. Main Applications Fasteners Fasteners. Industrial Cold Headed Parts, Heat Exchanger Shells, Pump Cylinder Liners Casting Characteristics. Typical Application: Metal goods, Deep drawn parts, Components for the electrical industry, Stamped parts, Connectors.
We are not liable for items out of stock. The specified weight is theoretical. Please contact us if you have any further enquiries.

Alloy - CW508L

Density
g/cm3
8.4
Cu
Min
62
Max
64
Al
Min
-
Max
0.05
Fe
Min
-
Max
0.1
Ni
Min
-
Max
0.3
Pb
Min
-
Max
0.1
Sn
Min
-
Max
0.1
Rest
Rest/Rem
Zn

Mechanical Properties - CW508L

RED Temper
R440
Thickness
Min
-
Max
5 mm
Tensile Strength
Min
440 N/mm2
Max
-
Proof Strength
Min
320 N/mm2
Max
-
Elongation Range (Elongation T > 2,5 - A% min)
Min
10
Max
-
Hardness (Vickers (HV))
Min
115
Max
-
RED Temper
R350
Thickness
Min
0.2 mm
Max
5 mm
Tensile Strength
Min
350 N/mm2
Max
440 N/mm2
Proof Strength
Min
170 N/mm2
Max
-
Elongation Range (Elongation T > 2,5 - A% min)
Min
28
Max
-
Hardness (Vickers (HV))
Min
95
Max
125
RED Temper
R410
Thickness
Min
0.2 mm
Max
5 mm
Tensile Strength
Min
410 N/mm2
Max
490 N/mm2
Proof Strength
Min
300 N/mm2
Max
-
Elongation Range (Elongation T > 2,5 - A% min)
Min
12
Max
-
Hardness (Vickers (HV))
Min
120
Max
155
RED Temper
R480
Thickness
Min
0.2 mm
Max
2 mm
Tensile Strength
Min
480 N/mm2
Max
560 N/mm2
Proof Strength
Min
430 N/mm2
Max
-
Elongation Range (Elongation T > 2,5 - A% min)
Min
-
Max
-
Hardness (Vickers (HV))
Min
150
Max
180
RED Temper
R300
Thickness
Min
0.2 mm
Max
5 mm
Tensile Strength
Min
300 N/mm2
Max
370 N/mm2
Proof Strength
Min
-
Max
180 N/mm2
Elongation Range (Elongation T > 2,5 - A% min)
Min
48
Max
-
Hardness (Vickers (HV))
Min
55
Max
95

Tolerances - CW508L

Thickness
Min
0.2 mm
Max
0.3 mm
Width
Min
700 mm
Max
1000 mm
Tolerance
Thickness ( +/- )
0.04 mm